西安鋼管低壓流體輸送用焊接鋼管和鍍鋅焊接鋼管的尺寸規(guī)格
|
公稱口徑 |
外 徑 |
普通鋼管 |
加厚鋼管 |
||||||
|
|
|
公稱尺寸／mm |
允許偏差 |
壁 厚 |
理論質(zhì)量／(k.g／m) |
壁 厚 |
理論質(zhì)量／(kg／m) |
||
|
公稱尺寸／mm |
允許偏差(％) |
公稱尺寸／mm |
允許偏差(％) |
||||||
|
6 |
1／8 |
10.0 |
|
2 .00 |
+12 -15 |
0.39 |
2.50 |
+12 -15 |
0.46 |
|
8 |
1／4 |
13.5 |
2.25 |
0.62 |
2.75 |
0.73 |
|||
|
10 |
3／8 |
17.0 |
|
2.25 |
0.32 |
2.75 |
0 97 |
||
|
15 |
1／2 |
21.3 |
2.75 |
1.26 |
3.25 |
1.45 |
|||
|
20 |
3／4 |
26.8 |
±0.50mm |
2.75 |
+12 -15 |
1.63 |
3.50 |
+12 -15 |
2.01 |
|
25 |
1 |
33.5 |
3.25 |
2.42 |
4.00 |
2.91 |
|||
|
32 |
1 1/4 |
42.3 |
3.25 |
3.13 |
4.00 |
3.78 |
|||
|
40 |
1 1/2 |
48.0 |
3.50 |
3.84 |
4.25 |
4.58 |
|||
|
50 |
2 |
60.0 |
±l％ |
3.50 |
4.88 |
4.50 |
6.16 |
||
|
65 |
2 1/2 |
75.5 |
3.75 |
6.64 |
4.50 |
7.88 |
|||
|
80 |
3 |
88.5 |
4.00 |
8.34 |
4.75 |
9.8l |
|||
|
l00 |
4 |
114.0 |
4.00 |
10.85 |
5.00 |
13.44 |
|||
|
125 |
5 |
140.0 |
4.00 |
13.42 |
5.50 |
18.24 |
|||
|
150 |
6 |
165.0 |
4.50 |
17.81 |
5.50 |
21.63 |
|||
1.表中的公稱口徑系近似內(nèi)徑的名義尺寸，不表示公稱外徑減去兩個(gè)公稱壁厚得的內(nèi)徑。
2.鋼管的通常長度為4—10m。鋼管按定尺、倍尺長度供應(yīng)時(shí)，允許偏差為+20mm。
3.鋼管用GB／T700規(guī)定的Q195、Q215和Q235A鋼制造。也可采用易焊接的其他軟鋼制造。其牌號(hào)由供方選擇。
4.鋼管用爐管和電焊方法制造。鍍鋅采用熱浸鍍鋅法。
5.鋼管不帶螺紋按原制造狀態(tài)交貨。根據(jù)需方要求，供需雙方協(xié)議，公稱口徑大于10mm的鋼管可帶螺紋交貨。
6.公稱直徑小于或等于50mm的鋼管應(yīng)進(jìn)行彎曲試驗(yàn)。彎曲試驗(yàn)時(shí)不帶填充物，黑管彎曲半徑等于鋼管公稱外徑的6倍，鍍鋅管應(yīng)等于外徑的8倍，彎曲角度為 90°，焊縫位于彎曲方向的側(cè)面。試驗(yàn)結(jié)果，試樣上不應(yīng)有裂縫及鋅層剝落現(xiàn)象。
7.鋼管應(yīng)進(jìn)行水壓試驗(yàn)，普通鋼管試驗(yàn)水壓為2.5MPa，加厚鋼管為3.0MPa。